Ca-P Conversion Coating on AZ60 Magnesium Alloy for Biomedical Application |
| |
Authors: | CHENG Zhongji ;LIAN Jianshe HU Xiaoli YANG Xiaohong LI Guangyu |
| |
Institution: | Key Laboratory of Automobile Materials, Ministry of Education, College of Materials Science and Engineering, Jilin University, Changchun 130022, P. R. China |
| |
Abstract: | To improve the anti-corrosion behaviors of magnesium alloy in the inner environment of human body, a bioactive Ca-P coating was deposited on the AZ60 magnesium alloy by a novel simple method. The morphologies of the Ca-P coatings formed under different treatment time were studied by scanning electron microscopy(SEM). The corrosion behaviors of Ca-P coating were investigated by electrochemical polarization test and electrochemical impedance spectroscopy in both 3%(mass fraction) NaCl solution and simulated body fluid(SBF). Immersion test in SBF was performed to evaluate the corrosion rate of Ca-P coated magnesium alloy. X-Ray diffraction(XRD) analysis result shows that the coating mentioned above mainly consists of dicalcium phosphate dehydrate(CaHPO4·2H2O, DCPD) and β-tricalcium phosphate dehydrateβ-TCP, Ca3(PO4)2], which exhibits good corrosion resistance. After magnesium alloy was immersed in 1 mol/L NaOH solution at 80℃ for 2 h, hydroxyapatite Ca10(PO4)6(OH)2, HA] appeared on the magnesium alloy substrate, which can further decrease the corrosion rate of AZ60 magnesium alloy in SBF. |
| |
Keywords: | Ca-P coating Deposited method Magnesium alloy Corrosion rate Simulated body fluid(SBF) |
本文献已被 维普 等数据库收录! |
| 点击此处可从《高等学校化学研究》浏览原始摘要信息 |
| 点击此处可从《高等学校化学研究》下载免费的PDF全文 |
|