KOH Direct Activation for Preparing Activated Carbon Fiber from Polyacrylonitrile-based Pre-oxidized Fiber |
|
| Authors: | GAO Lili LU Haiyan LIN Haibo SUN Xiuyun XU Jianling LIU Dechen LI Yang |
| Affiliation: | 1. College of Chemistry, Jilin University, Changchun 130012, P. R. China; 2. College of Chemistry and Pharmaceutical Engineering, Jilin Institute of Chemical Technology, Jilin 132022, P. R. China; 3. School of Environment, Northeast Normal University, Changchun 130117, P. R. China |
| Abstract: | The activated carbon fiber(ACF) was prepared from polyacrylonitrile-based pre-oxidized fiber(PANOF) by KOH direct activation. The influence of activation conditions including impregnation ratio(the mass ratio of PANOF to KOH), activation temperature and activation time on the pore structure and electrochemical properties of ACF was investigated, and the corresponding activation mechanism was proposed. The ACF prepared at an activation temperature of 800 ℃ and an impregnation ratio(the mass ratio of PANOF to KOH) of 1:2 for an activation time of 1 h in 6 mol/L KOH solution exhibits a specific surface area of 3029 m2/g, a mesoporosity of 84.2% and a specific capacitance of 288 F/g, and shows a good capacitive performance. The prepared ACF can be used as the electrode material for supercapacitors. |
| Keywords: | Direct activation KOH Activated carbon fiber Supercapacitor Polyacrylonitrile-based pre-oxidized fiber |
| 本文献已被 维普 等数据库收录！ | |
| 点击此处可从《高等学校化学研究》浏览原始摘要信息 | |
| 点击此处可从《高等学校化学研究》下载全文 | |