Zum Wachstum von AIIIBV-Halbleitern aus nichtstöchiometrischen Schmelzen (II) Dotierung von GaAs und Ga1−xAlxAs mit Zink

Doping of GaAs and Ga_1−xAl_xAs with Zn in the LPE process was studied by a radioanalytical method. It is found that Zn diffuses from the Ga-(Al)-As-Zn-solution into the n-GaAs substrate before epitaxial growth starts. This “pre-diffusion” and the following diffusion of Zn out of the epitaxial layer into the substrate results in three regions with distinct Zn-graduation in the vicinity of the pn-junction. There are no striking differences for GaAs/GaAs and Ga_1−xAl_xAs/GaAs structures. The Zn concentration in GaAs epitaxial layers decreases exponentially from the substrate up to the layer surface. From this profile the temperature dependence of the Zn segregation coefficient is calculated. At 900°C a value k_eff = 5,2 · 10⁻² is found. The doping profile in Ga_1−xAl/As layers is more complex. It is influenced by the changings of temperature during the growth of the layer and by the nonuniform Aldistribution over the layer thickness.