Evaluation of CO2 adsorption capacity of solid sorbents

The CO₂ adsorption capacity of the low-cost solid sorbents of waste tire char (TC) and chicken waste char (CW) was compared with commercial active carbon (AC) and 5 ? zeolite (ZA) using thermogravimetric analysis (TG), pressurized TG, and differential scanning calorimetry (DSC). The sorbents were degassed in a TG up to 150 °C to release all gases on the surface of the sample, then cooled down to the designed temperature for adsorption. TG results indicated that the CO₂ adsorption capacity of TC was higher than that of CW, but lower than those of AC and ZA. The maximum adsorption rate of TC at 50 °C was 0.61% min⁻¹, lower than that of AC, but higher than that of CW, 0.44% min⁻¹. The maximum adsorption rate of ZA at 50 °C was 3.1% min⁻¹. When the pressure was over 4 bar, the adsorption rate of ZA was lower than that of TC and AC. At 30 bar, the total CO₂ uptake of TC was 20 wt%, higher than that of CW and ZA but lower than that of AC. The temperature, nitrogen concentration, and water content also influenced the CO₂ adsorption capacity of sorbents to some extent. DSC results showed that adsorption was an exothermic process. The heat of CO₂ adsorption per mole of CO₂ of TC at 50 °C was 24 kJ mol⁻¹ while the ZA had the largest heat of adsorption at 38 kJ mol⁻¹. Comparing the characteristics of TC and CW, TC may be a promising sorbent for removal of CO₂.