Effects of alumina phases on CO2 sorption and regeneration properties of potassium-based alumina sorbents

A range of potassium-based alumina sorbents were fabricated by impregnation of alumina with K₂CO₃ to examine the effects of the structural and textural properties of alumina on the CO₂ sorption and regeneration properties. Alumina materials, which were used as supports, were prepared by calcining alumina at various temperatures (300, 600, 950, and 1,200 °C). The CO₂ sorption and regeneration properties of these sorbents were examined during multiple tests in a fixed-bed reactor in the presence of 1 vol% CO₂ and 9 vol% H₂O. The regeneration capacities of the potassium-based alumina sorbents increased with increasing calcination temperature of alumina. The formation of KHCO₃ increased with increasing calcination temperature during CO₂ sorption, whereas the formation of KAl(CO₃)(OH)₂, which is an inactive material, decreased. These results is due to the fact that the structure of alumina by the calcination temperature is related directly to the formation of the by-product [KAl(CO₃)(OH)₂]. The structure of alumina plays an important role in enhancing the regeneration capacity of the potassium-based alumina sorbent. Based on these results, a new potassium-based sorbent using δ-Al₂O₃ as a support was developed for post-combustion CO₂ capture. This sorbent maintained a high CO₂ capture capacity of 88 mg CO₂/g sorbent after two cycles. In particular, it showed a faster sorption rate than the other potassium-based alumina sorbents examined.