Influence of Compatibilizer-Type and Processing Approach on the Dispersion of OMMT in High-Density Polyethylene Matrix |
| |
Authors: | Amir Babaei S Reza Ghaffarian M Mehdi Khorasani Siamak Baseghi |
| |
Institution: | 1. Polymer Engineering Department , Amir Kabir University of Technology , Tehran , I. R. Iran;2. Amir Kabir University of Technology , Mahshahr Campus , Mahshahr , I. R. Iran;3. Polymer Engineering Department , Amir Kabir University of Technology , Tehran , I. R. Iran;4. Polymer Engineering Department , Amir Kabir University of Technology , Tehran , I. R. Iran |
| |
Abstract: | High-density polyethylene/organoclay nanocomposites were prepared via melt intercalation in an internal mixer using both a direct mixing and master batching method. Two types of maleic anhydride grafted polyethylene, high-density polyethylene grafted maleic anhydride, and linear low-density polyethylene grafted maleic anhydride, (HDPE-g-MA, LLDPE-g-MA) were used as compatibilizers to enhance the dispersibility of nanoclay in HDPE. Dispersion of organoclay in the nanocomposites was characterized by using X-ray diffraction (XRD), transmission electron microscopy (TEM), and rheological mechanical spectroscopy (RMS). Effects of clay content and degree of clay dispersion on the rheological and tensile properties were also investigated. Furthermore, the effect of order of mixing on the dispersion and distribution of the clay layers was studied. The obtained results showed that organoclay in the nanocomposites were dispersed homogeneously and exfoliated better when HDPE-g-MA and the direct mixing route were used. Although in the master batching method clay intercalated better, clay layers chiefly remain in compatibilizer rich areas. On the other hand, direct mixing was observed to lead to clay particles being dispersed in the HDPE matrix or at the interface of the matrix and compatibilizer and, consequently, better improvement in the tensile modulus was achieved. It was determined that the compatibilizer with the higher miscibility with the matrix was the key factor for achieving better exfoliation of clay sheets. |
| |
Keywords: | compatibilizer high-density polyethylene (HDPE) HDPE-g-MA melt intercalation nanocomposites order of mixing |
|
|