Preparation of poly(p‐oxybenzoyl) crystals using direct polymerization of p‐hydroxybenzoic acid in the presence of boronic anhydrides

Poly(p‐oxybenzoyl) (POB) crystals were prepared by reaction‐induced crystallization during direct polymerization of p‐hydroxybenzoic acid in the presence of boronic anhydrides. Polymerizations were carried out at 300 °C in dibenzyltoluene at a concentration of 1% with three kinds of anhydrides of boronic acid such as 3,4,5‐trifluorophenylboronic acid (TFB), 4‐methoxyphenylboronic acid (MPB) and 4‐biphenylboronic acid (BPB). The POB crystals were formed as precipitates in the solution and the morphology was considerably influenced by both the structure of the boronic anhydride and its concentration (c_B). Needle‐like crystals were firmed in the presence of TFB anhydride (TFBA) at c_Bs of 5 and 10 mol % by the spiral growth of lamellae. Spherical aggregates of slab‐like crystals were formed at c_Bs from 50 to 100 mol %. The polymerization with MPB anhydride and BPB anhydride (BPBA) also yielded the needle‐like crystals at c_Bs of 50 and 5 mol %, respectively. The polymerization with TFBA at lower c_B was favorable to prepare the needle‐like crystal. Molecular weight was also influenced by the structure of the boronic anhydride and c_B. M_n increased generally with c_B and BPBA gave the highest M_n of 14.7 × 10³ at c_B of 100 mol %. The loose packing of the molecules in the crystal caused by the bulkiness of the end‐groups made the polymerization in the crystals more efficiently. Morphology and molecular weight of the POB crystals could be controlled by the chemical structure and the content of boronic anhydride. © 2010 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem, 2011.