On the crystal chemistry of Tm2Ni1.896(4)In, Tm2.22(2)Ni1.81(1)In0.78(2), Tm4.83(3)Ni2In1.17(3), and Er5Ni2In

The rare earth-nickel-indides Tm₂Ni_1.896(4)In, Tm_2.22(2)Ni_1.81(1)In_0.78(2), Tm_4.83(3)Ni₂In_1.17(3), and Er₅Ni₂In were synthesized from the elements by arc-melting and subsequent annealing for the latter three compounds. Three indides were investigated by X-ray powder and single crystal diffraction: Mo₂FeB₂ type, P4/mbm, Z=2, a=731.08(4), c=358.80(3) pm, wR₂=0.0201, 178 F² values, 13 variables for Tm₂Ni_1.896(4)In, a=734.37(7), c=358.6(1) pm, wR₂=0.0539, 262 F² values, 14 variables for Tm_2.22(2)Ni_1.81(1)In_0.78(2), and Mo₅SiB₂ type, I4/mcm, a=751.0(2), c=1317.1(3) pm, wR₂=0.0751, 317 F² values, 17 variables for Tm_4.83(3)Ni₂In_1.17(3). X-ray powder data for Er₅Ni₂In revealed a=754.6(2) and c=1323.3(5) pm. The Mo₂FeB₂ type structures of Tm₂Ni_1.896(4)In and Tm_2.22(2)Ni_1.81(1)In_0.78(2) are intergrowths of slightly distorted CsCl and AlB₂ related slabs, however, with different crystal chemical features. The nickel sites within the AlB₂ slabs are not fully occupied in both indides. Additionally In/Tm mixing is possible at the center of the CsCl slab, as is evident from the structure refinement of Tm_2.22(2)Ni_1.81(1)In_0.78(2). The Mo₅SiB₂ type structures of Tm_4.83(3)Ni₂In_1.17(3) and Er₅Ni₂In can be considered as an intergrowth of distorted CuAl₂ and U₃Si₂ related slabs in an ABA′B′ stacking sequence along the c-axis. Again, one thulium site shows Tm/In mixing. The U₃Si₂ related slab has great structural similarities with the Mo₂FeB₂ type structure of Tm₂Ni_1.896(4)In and Tm_2.22(2)Ni_1.81(1)In_0.78(2). The crystal chemical peculiarities and chemical bonding in these intermetallics are briefly discussed.