Electrical properties of modified TZP(+TiO2,FeOx)

1 to 24 mol% TiO₂ and FeO_X were added to 3.2 mol% Y₂O₃ doped ZrO₂ (Z3Y) to obtain tetragonal zirconia polycrystals (TZP) with modified electronic properties. The materials were prepared by coprecipitation which allows to obtain fine, homogeneous and sinteractive powders. The solubility of TiO₂ in Z3Y can reach 24 mol%, while the maximum solubility of FeO_x is about 8 mol%. The impedance results show a decrease of the bulk and total conductivity of titania doped TZP with increasing titania concentration, while those of FeO_x doped TZP show only minor changes. The Hebb-Wagner polarization method was applied to evaluate the partial hole and electron conductivities. Three models are presented to interpret the polarization curves. 1.6 mol% FeO_x doped TZP has higher hole conductivity in air, while titania doped TZP has higher electronic conductivity at low oxygen partial pressures as compared to pure Z3Y. Paper presented at the 1st Euroconference on Solid State Ionics, Zakynthos, Greece, 11–18 Sept.1994