Industrial Materials Institute, National Research Council Canada, 75 de Mortagne Boulevard, Boucherville, QC, Canada J4B 6Y4
Abstract:
Ethylene-co-octene polymers containing different branching levels were irradiated in air and under vacuum at 25, 50 and 100 kGy. Gel fraction measurements, thermal analysis and rheology were used to assess the effect of the treatment on polymer structure modifications. The copolymer with 24 wt% octene was shown to be more sensitive to gamma rays and degradation was observed in some cases. Cross-linking in the amorphous phase also occurred as a consequence of irradiation and affected the foaming behavior of these materials.