In situ observation of NaBi(WO4)2 dendrite growth and the study on microstructure of solidification

The dendrite growth process of transparent NaBi(WO₄)₂ with small prandtl and high melting point was studied by using the in-situ observation system. According to the dynamic images and detailed information, there are two kinds of restriction effect on the dendrite growth, the competition between arms and branches and the convection in the melt. The dendrite growth rate was time dependent, and the rate of arm growth reached the maximum 5.8 mm/s in the diffusive-advective region and rapidly decreased in the diffusive-convective region. The growth rate of branch had the same change trends as the arm’s. Based on the EPMA-EDS data of solidification structure of quenched NaBi(WO₄)₂ melt, it was found that there were component differences from stoichiometric concentration in the melt near the interface during the growth process. Supported by the National Natural Science Foundation of China (Grant No. 50331040) and the Innovation Funds from Shanghai Institute of Ceramics, Chinese Academy of Sciences (Grant No. SCX0623)