Palladium Nanoparticles Embedded into Graphene Nanosheets: Preparation,Characterization, and Nonenzymatic Electrochemical Detection of H2O2

A novel nonenzymatic H₂O₂ sensor based on a palladium nanoparticles/graphene (Pd‐NPs/GN) hybrid nanostructures composite film modified glassy carbon electrode (GCE) was reported. The composites of graphene (GN) decorated with Pd nanoparticles have been prepared by simultaneously reducing graphite oxide (GO) and K₂PdCl₄ in one pot. The Pd‐NPs were intended to enlarge the interplanar spacing of graphene nanosheets and were well dispersed on the surface or completely embedded into few‐layer GN, which maintain their high surface area and prevent GN from aggregating. XPS analysis indicated that the surface Pd atoms are negatively charged, favoring the reduction process of H₂O₂. Moreover, the Pd‐NPs/GN/GCE could remarkably decrease the overpotential and enhance the electron‐transfer rate due to the good contact between Pd‐NPs and GN sheets, and Pd‐NPs have high catalytical effect for H₂O₂ reduction. Amperometric measurements allow observation of the electrochemical reduction of H₂O₂ at 0.5 V (vs. Ag/AgCl). The H₂O₂ reduction current is linear to its concentration in the range from 1×10^?9 to 2×10^?3 M, and the detection limit was found to be 2×10^?10 M (S/N=3). The as‐prepared nonenzymatic H₂O₂ sensor exhibits excellent repeatability, selectivity and long‐term stability.