Characterization of interface between CuInSe2 and In2O3

CuInSe₂/In₂O₃ structures were formed by depositing CuInSe₂ films by stepwise flash evaporation onto In₂O₃ films, which were grown by DC reactive sputtering of In target in presence of (Ar+O₂) gas mixture. Phase purity of the CuInSe₂ and In₂O₃ films was confirmed by Transmission Electron Microscopy (TEM) studies. X-ray diffraction (XRD) results on CuInSe₂/In₂O₃/glass structures showed sharp peaks corresponding to (112) plane of CuInSe₂ and (222) plane of In₂O_3. Rutherford Backscattering Spectrometry (RBS) investigations were carried out on CuInSe₂/In₂O₃/Si structures in order to characterize the interface between In₂O₃ and CuInSe₂. The results show that the CuInSe₂ films were near stoichoimetric and In₂O₃ films had oxygen deficient composition. CuInSe₂/In₂O₃ interface was found to include a ∼20 nm thick region consisting of copper, indium and oxygen. Also, the In₂O₃/Si interface showed the formation of ∼20 nm thick region consisting of silicon, indium and oxygen. The results are explained on the basis of diffusion/reaction taking place at the respective interfaces.