Blue and red long lasting phosphorescence (LLP) in β-Zn3(PO4)2:Mn,Zr

Multi-color long lasting phosphorescent (LLP) phenomenon in β-Zn₃(PO₄)₂:Mn²⁺,Zr⁴⁺ was systematically investigated. It is found that the red (λ_Em=616 nm) LLP performance of Mn²⁺ such as brightness and duration is largely improved, and that the blue (λ_Em=475 nm) LLP of Zr⁴⁺ with lower intensity appears when Zr⁴⁺ ions are co-doped into the matrix. The fluorescence, phosphorescence and thermoluminescence (TL) spectra show that Mn²⁺ ion is solely expected as a luminescent center, while Zr⁴⁺ ion not only acts as a luminescent center, but also induces an electron trap (Trap_Zr) associated with a TL peak at 344 K. The trap depth for Trap_Zr is 0.25 eV, while that for the intrinsic trap is 0.38 eV, associated with a dominant peak at 385 K for Zn₃(PO₄)₂:Mn²⁺. The Zr⁴⁺-induced trap with suitable depth is responsible for the improvement of the red LLP of Mn²⁺ ion and the appearance of the blue LLP of Zr⁴⁺ ion. The LLP mechanism is also investigated.