Abstract: | Quenched films of isotactic polypropylene were drawn at 110°C up to draw ratio λ = 18. The axial elastic modulus was measured as function of λ up to the highest achieved λ. The sorption and diffusion of CH2Cl2 at 25°C in the undrawn and drawn samples were studied. Exclusively transparent samples were used for the measurement of the density and transport properties. This reduces the maximum usable draw ratio to 15. The drawing process is inhomogeneous with neck propagation. In the neck the draw ratio increases by about 6. As a consequence of the increasing fraction of taut tie molecules the axial elastic modulus increases faster than the draw ratio. The transport parameters D, S, and λ indicate that the original lamellar morphology is completely transformed into the microfibrillar structure. |