| Abstract: | Small-angle light-scattering (SALS) studies were carried out on block copolymers of poly(ethylene terephthalate) (PET) and poly(butylene terephthalate) (PBT), the synthesis and characterization of which have been reported in an earlier paper. Samples were crystallized isothermally from the melt at 95°C for predetermined crystallization times in order to follow the formation and growth of crystalline superstructure. During the early stages of crystallization, the block copolymers showed unusual Hv patterns with the four lobes along the polarizer directions, while at later stages they showed the usual Hv patterns with the four lobes at 45° to the polarizer directions. The unusual patterns are characteristic of PBT superstructure, while the usual patterns are characteristic of PET superstructure. These results show that PBT, which is the faster-crystallizing component, crystallizes first and provides nucleation sites for the crystallization of PET, which crystallizes later. Similar behavior was not observed in PET homopolymer and random copolymers of equivalent compositions. In each case the spherulite size increased with the time of crystallization. The ultimate spherulite size decreased with increasing PBT content in the block copolymer, thus showing an increase in nucleation density. It was demonstrated that light scattering is a useful tool to characterize block copolymers of two crystalline components which have different types of superstructure. |