Magnetic properties and structural chemistry of ternary silicides (RE,Th, U)Ru2Si2 (RE = RARE EARTH)

Ternary silicides (RE, Th, U)Ru₂Si₂ have been synthesized from the elements. All the compounds (RE = Y, La, Ce, Pr, Nd, Sm, Gd, Tb, Dy, Ho, Er, Tm, Yb, Lu) were found to be isotypic and to crystallize with the structure type of ThCr₂Si₂ (ordered derivative of the BaAl₄-type). The magnetic behavior of these alloys was studied in the temperature range 1.5 K < T < 1100 K. Magnetic susceptibilities at temperatures T > 300 K closely follow a typical Van Vleck paramagnetism of free RE³⁺-ions. In the case of CeRu₂Si₂ susceptibilities are well described for 20 K < T < 1100 K by a Van Vleck paramagnetism of widely spaced multiplets; the observed effective paramagnetic moment μ_eff = 2.12 BM indicates a high percentage (85%) of Ce³⁺. SmRu₂Si₂ yields an effective moment μ_eff = 0.54 BM, which compares reasonably well with the Hund's rule J = 5/2 ground level for free Sm⁺ and a low-lying excited level with J = 7/2. For temperatures T > 15 K the magnetic susceptibility as a function of temperature follows the “Van Vleck behavior” for free Sm³⁺. At low temperatures ferromagnetic ordering was encountered for (Pr, Nd, Ho, Er, Tm)Ru₂Si₂, whereas antiferromagnetic ordering was observed for (Sm, Gd, Tb, Dy)Ru₂Si₂. The ordering temperatures are generally below 55 K. No superconductivity was found for temperatures as low as 1.8 K.