Thermal and mechanical behavior of polyethylene film obtained by orientational crystallization |
| |
| Authors: | M. Z. El Sabee W. G. Perkins R. S. Porter V. G. Baranov S. Ya. Frenkel |
| |
| Affiliation: | (1) Materials Research Laboratory Polymer Sciences Engineering Department, University of Massachusetts Amherst, 01003 Massachusetts, USA;(2) Institute of Macromolecular Compounds, 199004 Leningrad, U S S R;(3) Present address: Chemistry Department, Faculty of Science, Cairo University, Egypt |
| |
| Abstract: | The thermal and mechanical behaviour was measured in the U. S.for a polyethylene that had been prepared and highly drawn in the U. S. S. R. The melting point and percent crystallinity were evaluated in this studies as a function of heating rate and recrystallization. The Young's modulus and tensile stress to break in the orientation direction were 4.1 and 0.15 GPa, respectively.The tensile strain to break was about 8%.
Zusammenfassung Das thermische und mechanische Verhalten eines in der UdssR hergestellten und stark gezogenen Polyäthylens wurde in den U. S. A. gemessen. Schmelzpunkt und Prozentsatz der Kristallinität wurden als Funktion der Aufheizgeschwindigkeit und Rekristallisation in den Untersuchungen ausgewertet. Der Young-sche Modulus und die Zugspannung zum Reissen in der Orientierungsrichtung betrugen 4.1, bzw. 0.15 GPa. Die Dehnung bis zum Bruch betrug etwa 8 %.
Résumé On a effectué, aux Etats Unis, l'étude du comportement thermique et mécanique d'un polyéthylène préparé et fortement étiré en URSS. Le point de fusion et le pourcentage de cristallinité ont été évalués en fonction de la vitesse de chauffage et de la recristallisation. Lesvaleurs respectives du module d'Young et de la limite de rupture dans la direction d'orientation s'élèvent respectivement à 4.1 et 0.15 GPa. L'allongement à la rupture est d'environ 8%.
                             , .    .   .   4.1 0.15   .   8%.
|
| |