Thermal and hydrolytic stability of sulfonated polyimide membranes with varying chemical structure |
| |
Authors: | Wonbong Jang Choonkeun Lee Saimani Sundar Yong Gun Shul Haksoo Han |
| |
Institution: | aDepartment of Chemical Engineering, Yonsei University, 134 Shinchon-dong, Sedaemun-gu, Seoul 120-749, Republic of Korea beMD Lab, SAMSUNG Electro-Mechanics Co., 314 Maetan3-dong, Yeongtong-gu, Suwon, Gyunggi-do 443-743, Republic of Korea cYonsei Center for Clean Technology, Yonsei University, 134 Shinchon-dong, Sedaemun-gu, Seoul 120-749, Republic of Korea |
| |
Abstract: | Many important properties required for fuel cell applications including hydrolytic stability, depend on various factors like flexibility of the polymer backbone, ring structure and phase separation. This paper is primarily focused on studying the effect of the chemical backbone structure on the hydrolytic stability and other properties. To study the difference in the hydrolytic stability with change in the chemical backbone structure of sulfonated polyimides we synthesized phthalic sulfonated polyimides and naphthalenic sulfonated polyimides. Two series of phthalic sulfonated polyimides were prepared using 4,4′-oxydiphthalic anhydride (ODPA) and 4,4′-methylene dianiline (MDA), and 4,4′-(hexafluoroisopropylidine) diphthalic anhydride (6FDA) and oxydianiline (ODA). 4,4′-Diaminobiphenyl-2,2′-disulfonic acid (BDSA) was used to introduce sulfonic acid group into both series. Naphthalenic polyimides were synthesized from 1,4,5,8-naphthalenetetra-carboxylic dianhydride, BDSA, MDA and ODA. Also to observe other properties according to variation of sulfonic acid content, the degree of functionalisation was effectively controlled by altering the mole ratio between the sulfonated and non-sulfonated diamine monomers in phthalic sulfonated polyimides. The hydrolytic stability of the polyimides was followed by FT-IR spectroscopy at regular intervals. Polyimides prepared using naphthalenic dianhydride, NTDA, exhibited higher hydrolytic stability than the phthalic dianhydrides. The proton conductivity, ion exchange capacity (IEC) and water uptake measurements revealed the dependence on the molecular weight of the repeating unit. The proton conductivity of the sulfonated polyimides was found to vary with chemical backbone structure. |
| |
Keywords: | Sulfonated polyimides Hydrolytic stability Morphology Proton conductivity Fuel cells |
本文献已被 ScienceDirect 等数据库收录! |
|