Development of rf plasma sputtered Al2O3-TiO2 multilayer broad band antireflecting coatings and its correlation with plasma parameters

TiO₂/Al₂O₃/TiO₂/Al₂O₃ multilayer structures were obtained at different oxygen:argon gas ratios of 20:80, 30:70, 50:50 and 60:40 sccm and constant rf power of 200 W using reactive magnetron sputtering. Grain size and elemental distribution in the films were studied from AFM image and XPS spectra respectively. The deposited grain size increased with increasing oxygen:argon gas ratio. The optical band gap, refractive index, extinction coefficient were calculated from UV-vis transmittance and reflectance spectra. It was observed that the value of refractive index, extinction coefficient and band gap increased with increasing oxygen. These variations are due to the defects levels generated by the heterostructure and explained by the PL spectrum. The antireflecting (AR) efficiency of the films was estimated from the reflectance spectra of the films. Broad band antireflecting coating for the visible range was achieved by varying oxygen content in the film. The plasma chemistry controlled the antireflecting property by the interface interdiffusion of atoms during layer transition in multilayer deposition. The in situ investigation of the plasma chemistry was performed using optical emission spectroscopy. The plasma parameters were estimated and correlated with the characteristics of the films.