Thickness measurement of a thin hetero-oxide film with an interfacial oxide layer by X-ray photoelectron spectroscopy

The general equation T_ove = L cos  θ ln(R_exp/R₀ + 1) for the thickness measurement of thin oxide films by X-ray photoelectron spectroscopy (XPS) was applied to a HfO₂/SiO₂/Si(1 0 0) as a thin hetero-oxide film system with an interfacial oxide layer. The contribution of the thick interfacial SiO₂ layer to the thickness of the HfO₂ overlayer was counterbalanced by multiplying the ratio between the intensity of Si⁴⁺ from a thick SiO₂ film and that of Si⁰ from a Si(1 0 0) substrate to the intensity of Si⁴⁺ from the HfO₂/SiO₂/Si(1 0 0) film. With this approximation, the thickness levels of the HfO₂ overlayers showed a small standard deviation of 0.03 nm in a series of HfO₂ (2 nm)/SiO₂ (2-6 nm)/Si(1 0 0) films. Mutual calibration with XPS and transmission electron microscopy (TEM) was used to verify the thickness of HfO₂ overlayers in a series of HfO₂ (1-4 nm)/SiO₂ (3 nm)/Si(1 0 0) films. From the linear relation between the thickness values derived from XPS and TEM, the effective attenuation length of the photoelectrons and the thickness of the HfO₂ overlayer could be determined.