Green Template‐Free Synthesis of Hierarchical Shuttle‐Shaped Mesoporous ZnFe2O4 Microrods with Enhanced Lithium Storage for Advanced Li‐Ion Batteries

In the work, a facile and green two‐step synthetic strategy was purposefully developed to efficiently fabricate hierarchical shuttle‐shaped mesoporous ZnFe₂O₄ microrods (MRs) with a high tap density of ～0.85 g cm³, which were assembled by 1D nanofiber (NF) subunits, and further utilized as a long‐life anode for advanced Li‐ion batteries. The significant role of the mixed solvent of glycerin and water in the formation of such hierarchical mesoporous MRs was systematically investigated. After 488 cycles at a large current rate of 1000 mA g^?1, the resulting ZnFe₂O₄ MRs with high loading of ～1.4 mg per electrode still preserved a reversible capacity as large as ～542 mAh g^?1. Furthermore, an initial charge capacity of ～1150 mAh g^?1 is delivered by the ZnFe₂O₄ anode at 100 mA g^?1, resulting in a high Coulombic efficiency of ～76 % for the first cycle. The superior Li‐storage properties of the as‐obtained ZnFe₂O₄ were rationally associated with its mesoprous micro‐/nanostructures and 1D nanoscaled building blocks, which accelerated the electron transportation, facilitated Li⁺ transfer rate, buffered the large volume variations during repeated discharge/charge processes, and provided rich electrode–electrolyte sur‐/interfaces for efficient lithium storage, particularly at high rates.