Oxide cathodes for electrochemical devices made with the use of a nanostructured composition material

The possibility of using the LnO _x mischmetal (Ln = Ce, La, Nd, Pr, Sm) for preparation of cathodes for solid-oxide fuel cells with the supported YSZ electrolyte is studied. The electrical and electrochemical characteristics of Ln-Mn-O electrodes with the ratio of all lanthanides contained in the mischmetal except for cerium to manganese Ln: Mn = 1: 1 and also of a material comprised of Ln-Mn-O and La_0.8Sr_0.2MnO₃ are studied. The latter electrode material that contains 35?C40 wt % of Ln-Mn-O and was sintered at 1200°C has the specific ohmic resistance of 0.1 ?? cm at 800°C. The polarization conductivity is compared for electrodes made of 100% Ln-Mn-O, 40 wt % Ln-Mn-O + 60 wt % La_0.8Sr_0.2MnO₃, and 100% La_0.8Sr_0.2MnO₃ in the initial state and after their modification through the introduction of an electrocatalyst (PrO_{2 ? x} ). The highest polarization conductivity is typical of Ln-Mn-O + (La, Sr)MnO₃ electrodes containing 40 wt % Ln-Mn-O and PrO_{2 ? x} . The polarization conductivity of these electrodes is found to be 25 S/cm² at 800°C.