Crystal growth,spectroscopic characteristics,and Judd–Ofelt analysis of Dy:Lu_2O_3 for yellow laser |
| |
作者姓名: | 施佼佼 刘斌 王庆国 唐慧丽 吴锋 李东振 赵衡煜 王占山 邓文 徐晓东 徐军 |
| |
摘 要: | Dy:Lu_2O_3 was grown by the float-zone(Fz) method. According to the absorption spectrum, the Judd–Ofelt(JO) parameters ?_2, ?_4, and ?_6 were calculated to be 4.86 × 10~(-20) cm~2, 2.02 × 10~(-20) cm~2, and 1.76 × 10~(-20) cm~2, respectively.The emission cross-section at 574 nm corresponding to the ~4F6_(9/2)→~6H_(13/2) transition was calculated to be 0.53 × 10~(-20) cm~2.The yellow(~4F_(9/2)→~6H_(13/2) transition) to blue(~4F_(9/2)→~6H_(15/2) transition) intensity ratio ranges up to 12.9. The fluorescence lifetime of the ~4F_(9/2) energy level was measured to be 112.1 μs. These results reveal that Dy:Lu_2O_3 is a promising material for use in yellow lasers.
|