Three-dimensional atom probe study of the segregation behaviour of Ni91Pt9 alloy after sputtering

To investigate local ordering and segregation phenomenon in a Ni91Pt9-alloy after sputtering and annealing a 3D optical atom probe (OAP) has been used. The specimen tips have been prepared from polycrystalline samples. To sputter the samples a separate preparation chamber with a scannable Ar-sputter-gun is connected to the OAP vessel. When necessary, the sample can be electrically heated to induce segregation and cure the altered layer. After a heat treatment of a Ni91 at. %Pt 9 at.% specimen at 1100 K the surface of a (111)-oriented specimen is enriched in platinum by a factor of two in relation to the bulk. The phenomenon of short-range ordering has been investigated on the surface and in the subsurface volume. A 3D reconstruction of this annealed NiPt specimen shows regions with high concentration of platinum that gives an indication at short-range ordering. Uniform sputtering of the tip without a heat treatment induces a decisive depletion of Pt on the surface and the following subatomic layers. The atom-probe results of specimens in thermal equilibrium are in close agreement to further surface sensitive results obtained from Ion Scattering Spectroscopy (ISS) and Auger Electron Spectroscopy (AES).