Interface characterization in latex blend films by fluorescence energy transfer

Immiscible polymer blend films were formed by air drying aqueous dispersions containing mixtures of a high-T_g latex, poly(methyl methacrylate), and a film-forming low-T_g latex, poly(butyl methacrylate-co-butyl acrylate). Fluorescence energy transfer experiments were used to characterize the interfaces in these films, in which one component was labeled with a donor dye and the other with an acceptor. The quantum efficiency of energy transfer (Φ_ET) between the donors and acceptors is influenced by the interfacial contact area between the two polymer phases. As the amount of soft component in the blend is increased, Φ_ET approaches an asymptotic value, consistent with complete coverage of the hard polymer surface with soft polymer. This limiting extent of energy transfer is very sensitive to the total surface area in the film, with correspondingly more energy transfer at constant volume fraction for small hard particles. Some of the details of the energy transfer are revealed through a fluorescence lifetime distribution analysis. The presence of ionic surfactant (sodium dodecyl sulfate) in the dispersion from which the latex blend film is prepared reduces the cross-boundary energy transfer by 30%, which implies that in these films the surfactant decreases the interfacial contact. After annealing the surfactant-free blends above 100°C, we observe an increase in energy transfer, consistent with a broader interface between the two polymers. © 1998 John Wiley & Sons, Inc. J Polym Sci B: Polym Phys 36: 1115–1128, 1998