| Abstract: | Fatigue crack growth studies in rail steels and associated weld metal have shown that (a) deformed rail steel exhibited fatigue crack growth rates that are slightly faster than undeformed rail steel and (b) weld metal growth data are appreciably faster than rail steel growth results and exhibit growth rate plateaux that reside above the upper bound reported for rail steel fatigue crack growth.In rail steel microstructures at low ΔK levels fatigue crack extension occurred by a ductile striated growth mechanism. However at Kmax values approaching 40 MPa √m transgranular cleavage facets initially formed and their incidence increased with Kmax until final fast fracture. The average cleavage facet size agreed well with pearlite nodule dimensions of 60–100 μm.The weld metal microstructure was much coarser than the rail steel and contained highly directional columnar grain growth. At all ΔK levels the dominant fracture mode was transgranular cleavage containing small isolated regions of ductile striated fatigue crack growth. The cleavage facet size varied from 150 to 600 μm; such a large variation was explained by the fact that in general crack extension tended to occur in association with the proeutectoid ferrite phase. |