| 蒙脱土填充聚丙烯复合材料的摩擦磨损行为研究 |
| |
| 引用本文： | 陈奎,杨瑞成,成生伟.蒙脱土填充聚丙烯复合材料的摩擦磨损行为研究[J].摩擦学学报,2006,26(6):561-565. |
| |
| 作者姓名： | 陈奎 杨瑞成 成生伟 |
| |
| 作者单位： | 1. 兰州理工大学 甘肃省有色金属新材料省部共建国家重点实验室,甘肃 兰州 730050;兰州理工大学 有色金属合金省部共建教育部重点实验室,甘肃 兰州 730050;中国科学院兰州化学物理研究所固体润滑国家重点实验室,甘肃 兰州 730000
2. 兰州理工大学 甘肃省有色金属新材料省部共建国家重点实验室,甘肃 兰州 730050;兰州理工大学 有色金属合金省部共建教育部重点实验室,甘肃 兰州 730050 |
| |
| 基金项目： | 甘肃省自然科学基金资助项目（ZS021-A25-028-C）. |
| |
| 摘 要： | 采用熔体插层法在双螺杆挤出机上制备出含不同质量分数的有机蒙脱土（OMMT）PP复合材料，对OMMT／PP复合材料的力学性能和摩擦磨损性能进行研究，利用扫描电子显微镜观察磨损表面性貌．结果表明：复合材料的硬度和拉伸强度随OMMT含量增加先增加后减小；Ⅴ型缺口冲击强度逐渐上升；摩擦系数和磨损率先降低而后升高；当OMMT质量分数为1．5％时，复合材料的硬度和拉伸强度最大，磨损率为PP的65％，摩擦系数降低8．5％；随着OMMT含量增加（0％～4％），复合材料的磨损形式主要为粘着磨损、磨粒磨损以及粘着磨损与磨粒磨损的混合形式．
|
| 关 键 词： | 蒙脱土／聚丙烯复合材料 力学性能 摩擦磨损性能 |
| 文章编号： | 1004-0595（2006）06-0561-05 |
| 收稿时间： | 2005-12-24 |
| 修稿时间： | 2005-12-242006-03-27 |
Research on Tribological Behavior of OMMT/Polypropylene Composites |
| |
| CHEN Kui,YANG Rui-cheng,CHENG Sheng-wei.Research on Tribological Behavior of OMMT/Polypropylene Composites[J].Tribology,2006,26(6):561-565. |
| |
| Authors: | CHEN Kui YANG Rui-cheng CHENG Sheng-wei |
| |
| Institution: | 1. State Key Laboratory of Gansu Advanced Non-ferrous Metal Materials, Lanzhou University of Technology, Lanzhou 730050, China ; 2. Key Laboratory of Non-ferrous Metal Alloys, Ministry of Education, Lanzhou University of Technology, Lanzhou 730050, China; 3. State Key Laboratory of Solid Lubrication, Lanzhou Institute of Chemical Physics, Chinese Academy of Sciences, Lanzhou 730000, China |
| |
| Abstract: | OMMT/PP composites were synthesized through melt intercalation in twin-screw extruder.The effects of the content of OMMT on the hardness,tensile strength and notch impact strength of the composites were investigated.The friction and wear behavior of the composites sliding against GCr15 steel under 250 N was examined on M-2000 test rig in a ring-on-block configuration.The worn surfaces of the composites were examined by scanning electron microscopy.Composites containing 1.5% OMMT exhibited high tensile strength,hardness and much better friction and wear behavior than that of PP matrix.With increasing of OMMT content(0%~4%),wear of the composites was dominated by adhesive wear,abrasive and adhesive wear mixed abrasive wear respectively. |
| |
| Keywords: | polypropylene/montmorillonite composites mechanical property friction and wear behavior |