苯乙炔封端的可交联含氟聚芳醚的合成及性能

从光电集成器件对于材料性能的需要出发 ,我们相继合成了一系列可溶性的含氟聚芳醚和聚芳醚酮1～ 5] .为了满足器件的多层化制备过程以及使器件成型后具有优异的性能 ,本文在间三氟甲基苯取代的聚芳醚 (1 1 F- PAE)中引进可交联的苯乙炔端基 ,合成了可热交联的高含氟量聚芳醚 ,并对其性能进行了初步研究 .1　实验部分1 .1　试剂与仪器　 4-苯乙炔苯酚 (PEP)按文献 6 ]方法制备 ;3 -氟甲基苯代对苯二酚 (3 F- PH)按文献2 ]方法制备 ;十氟联苯 ,Aldrich公司 ,99%;无水碳酸钾 ,A.R.级 ,天津化学试剂厂 ;甲苯 ,A.R.级 ,北京化工厂 ;N-…

Synthesis and Properties of Crosslinkable Fluorinated Poly(aryl ethers)Terminated with Phenylethynyl Moieties

The crosslinkable trifluoromethylated poly(aryl ethers) terminated with phenylethynyl moieties(11F-PAE-PEP)s were prepared in two step syntheses. The structure of 11F-PAE-PEP was confirmed by FTIR and 1H NMR. The crosslinking behavior was studied by DSC. There is a remarkable increase of T g after crosslinking of the poly(aryl ethers). The T g values of crosslinked polymers were 437 and 446 K, respectively. The crosslinked polymers could not be soluble in common organic solvents, such as N,N-dimethylformamide, N,N-dimethylacetamide, N-methyl-2-pyrrolidinone, chloroform, and tetrahydrofuran. The temperatures at a 5% mass loss of the crosslinked polymers in air were above 789 K. They showed a good optical property, too. This kind of polymers will be the promising materials used as the microelectronics and optical waveguide devices.