Effect of pulsed laser parameters on in-situ TiC synthesis in laser surface treatment |
| |
Authors: | M.J. Hamedi M.J. TorkamanyJ. Sabbaghzadeh |
| |
Affiliation: | Iranian National Center for Laser Science and Technology, Tehran, Iran |
| |
Abstract: | Commercial titanium sheets pre-coated with 300-μm thick graphite layer were treated by employing a pulsed Nd:YAG laser in order to enhance surface properties such as wear and erosion resistance. Laser in-situ alloying method produced a composite layer by melting the titanium substrate and dissolution of graphite in the melt pool. Correlations between pulsed laser parameters, microstructure and microhardness of the synthesized composite coatings were investigated. Effects of pulse duration and overlapping factor on the microstructure and hardness of the alloyed layer were deduced from Vickers micro-indentation tests, XRD, SEM and metallographic analyses of cross sections of the generated layer. Results show that the composite cladding layer was constituted with TiC intermetallic phase between the titanium matrix in particle and dendrite forms. The dendritic morphology of composite layer was changed to cellular grain structure by increasing laser pulse duration and irradiated energy. High values of the measured hardness indicate that deposited titanium carbide increases in the conditions with more pulse duration and low process speed. This occurs due to more dissolution of carbon into liquid Ti by heat input increasing and positive influence of the Marangoni flow in the melted zone. |
| |
Keywords: | Pulsed Nd:YAG laser Composite coating Titanium carbide Microhardness Morphology |
本文献已被 ScienceDirect 等数据库收录! |