Direct observations of La ordering and domain structures in La0.61Li0.17TiO3 by high resolution electron microscopy

La_0.61Li_0.17TiO₃ microstructures have been studied by high resolution electron microscopy. A local lattice distortion occurs in the vicinity of the domain boundary region due to the twin with an angle of 89°. The average domain size of La_0.61Li_0.17TiO₃ is greater than 20 nm. The domain size and structures of La_0.61Li_0.17TiO₃ differ greatly from those of La-poor compounds, such as La_0.55Li_0.35TiO₃. At a nanoscopic level, microdomains of 20–100 nm in size construct a two-dimensional structure in La-rich compounds, while microdomains of 5–10 nm in size construct a three-dimensional structure in La-poor compounds. In addition, the Li-ion conduction mechanisms for La-rich and La-poor compounds are two- and three-dimensional, respectively.