Crystallite orientation in stretched polychloroprene networks. II

The orientation of crystallites grown isothermally in several drawn trans-polychloroprene networks is studied as a function of crystallization temperature t_x, degree of crystallinity ω, and elongation ratio α. The orientation distribution is particularly simple for this polymer since the crystallographic c axis (chain axis) orients preferentially along the stretching direction, while a and b are randomly arranged about c. Hence the parameter cos² χ_c adequately characterizes the distribution, where χ_c is the angle between the c axis and the fiber axis, and the average is taken over all crystallites. A treatment due to Krigbaum and Roe is utilized to obtain values of v (the number of statistical segments comprising the crystallization nucleus of critical size) through comparison of the average orientation of crystallites and amorphous statistical segments. The behavior observed falls into two categories. First, if the initial amorphous network is well oriented, 〈cos² χ_c〉 is independent of crystallinity during both crystallization and melting, and v varies with t_z (or the degree of supercooling) as predicted by nucleation theory. If different networks are to have the same crystallite orientation distribution, they must not only be crystallized at the same supercooling, but must also have the same distribution of amorphous segment orientations. Both the relative elongation and the network crosslink density affect the latter distribution. Next, we consider the second category. If the initial amorphous orientation is poor, 〈cos² χ_c〉 decreases linearly during crystallization and increases along approximately the same path during melting. Further, 〈cos² χ_c〉 for a given t_z yields v values which are too large. These two behaviors can be explained if, in the former case, nucleation involves the best oriented statistical segments of all network chains, while in the latter there is a selection according to the chain displacement vector orientation. Thus, if the amorphous orientation is poor, both the orientation and thermodynamic stability of the crystallites decreases with further crystallization. If this decreased stability is reflected in shorter fold lengths, the reversible variation of long period spacing with temperature reported earlier for an oriented polychloroprene network can also be explained as a preferential melting process.