On the structure of glassy polymers. II. Small-angle x-ray scattering from poly(methyl methacrylate)
Authors:A L Renninger  D R Uhlmann
Abstract:The small-angle x-ray scattering (SAXS) from glassy poly(methyl methacrylate) has been measured using a Bonse–Hart system. The data cover the angular range (2θ) between 20 sec and 2 deg. After correcting for absorption, background, and beam divergence, the data have been placed on an absolute basis by comparison with the scattering from a standard silica suspension. The corrected absolute intensity decreases strongly with increasing angle over the range between 20 sec and 30 min, and is nearly constant between 30 min and 2 deg. The magnitude of the scattering in the constant range, 0.6 (electrons)2 Å?3, is within a factor of 1.5 of the value predicted by the thermodynamic fluctuation theory for fluids applied at the glass transition temperature. The increase in intensity at smaller angles cannot be described by structures on the scale of the nodules reported in highly isotactic PMMA (150–200 Å), but can be well represented by small concentrations of heterogeneities, several thousand angstrom units in size, superimposed on the thermal density fluctuations frozen-in at the glass transition. The bulk structure of this material is well described as a random amorphous solid, containing simple thermal fluctuations and a small concentration of relatively large heterogeneities.
Keywords:
设为首页 | 免责声明 | 关于勤云 | 加入收藏

Copyright©北京勤云科技发展有限公司  京ICP备09084417号