Characterizations of white-light ZnWO4 phosphor prepared by blending complementary phosphor

In the preparation of ZnWO₄ phosphor, crystalline ZnWO₄ was created, even though the concentration of WO₃ was only 10 mol%. ZnWO₄ was the dominant crystallization phase when the concentration of WO₃ exceeded 40 mol%. The optimal crystallization of ZnWO₄ phosphor was obtained when the composition molar ratio of ZnO to WO₃ was 1:1, and sintering was carried out at 1,100°C for 3 h. In this condition, a bluish-green emission with a peak at 460 nm was observed. For Y₂O₃:Eu³⁺,Li⁺, the complementary phosphor of ZnWO₄, the Li flux improved phosphor crystallization. The red emission peak of the Y₂O₃:Eu³⁺,Li⁺ phosphor was measured at about 612 nm. The optimal photoluminescence intensity of the Y₂O₃:Eu³⁺,Li⁺ phosphor was obtained when it was sintered at 1,200°C for 5 h and was mixed with 11 mol% Eu₂O₃ and 70 mol% Li₂CO₃. When the weight ratio of Y₂O₃:Eu³⁺,Li⁺ to ZnWO₄ was 1:4, the Y₂O₃:Eu³⁺,Li⁺-blended ZnWO₄ phosphor showed white-light emission with Commission Internationale de l’Eclairage coordinates at (0.34, 0.30). The luminance of the white-light phosphor excited by a 6-W UV lamp was around 160 cd/m².