Phase equilibria and oxidation mechanisms in the LA-S-O system |
| |
Authors: | Y. Kitazawa Y. Kunimoto M. Wakihara M. Taniguchi |
| |
Affiliation: | (1) Department of Chemical Engineering, Tokyo Institute of Technology, Ookayama, Meguro-ku, 152 Tokyo, Japan |
| |
Abstract: | The phase diagram of the La-S-O system at 1073 K was established with the vacuum seal technique. Six phases exist at this temperature: La2O3 (B-type), LaS2, La2S3, La2O2SO4, La2O2S and La2O2S2. The thermodynamic functions for the reaction La2O2SO4=La2O3+SO2+1/2 O2 were determined by using the emf method at temperatures from 1123 to 1373 K. The mechanisms of the oxidation reactions in the La-S-O system under different partial pressures of oxygen (–4.4 < log <–0.7) were also investigated by means of DTA, TG and powder X-ray diffractometry.
Zusammenfassung Das Phasendiagramm des La-S-O-Systems bei 1073 K wurde bestimmt. Bei dieser Temperatur liegen 6 Phasen vor, und zwar La2O3 (B-Typ), LaS2, La2S3, La2O2SO4, La2O2S und La2O2S2. Für die Reaktion La2O2SO4=La2O3+SO2+1/2 O2 wurden die thermodynamischen Funktionen im Temperaturbereich von 1123–1373 K nach der EMF-Methode bestimmt. DTA, TG und Pulver-Röntgendiffraktometrie wurden zur Untersuchung der Mechanismen der im La-S-O-System verlaufenden Oxydationsreaktionen herangezogen, wobei der Sauerstoffpartialdruck in den Grenzen von – 4.4 < log < <-0.7 variiert wurde.
La-S-O 1073 . : La2O3 (-), LaS2, La2S3, La2O2SO4, La2O2S La2O2S2. . . ., La2O2SO4=La2O3+ SO2+1/2 2 1123–1373. , La-S-O –4.4 < log< –0.7. |
| |
Keywords: | |
本文献已被 SpringerLink 等数据库收录! |
|