金属玻璃(Fe0.8Ni0.15Cr0.05)78Si8B14的起始磁导率减落现象

在77—553K范围内的不同温度下测量了金属玻璃(Fe_0.8Ni_0.15,Cr_0.05)₇₈Si₈B₁₄的起始磁导率减落。测量结果表明,减落的温度关系表现为一个具有单一弛豫峰的不对称谱。在273K下考察了减落的动力学行为。用Hesse-Rubartsch方法拟合动力学曲线得到一个左右不对称的单峰激活能谱,最可几激活能大约为1.40eV。考察了减落的退火效应及退火动力学行为,结果表明,在宽的温度范围内,减落呈现明显的退火效应,而且退火动力学行为近似服从lnt动力学。关键词：

DISACCMMODATION PHENOMENON IN METALLIC GLASS (Fe0.8Ni0.15Cr0.05)78Si8B14

Disaccommodation (DA) of initial permeability of metallic glass (Fe_0.8Ni_0.15Cr_0.05)₇₈Si₈B₁₄ was measured at various temperatures in the range of 77-553 K. The measurements have shown that DA exhibits an asymmetric spectrum with a single relaxation peak. Kinetic behaviour of DA was examined at 273 K. An asymmetric activation energy spectrum with a single peak and the most probable activation energy of 1.40 eV was obtained by fitting a kinetic curve of DA by means of Hesse-Rubartsch's method. Effect of annealing on DA and kinetic behaviour of the annealing were examined. It was shown that the annealing essentially affects on DA and the kinetice behaviour of the annealing is approximateiy governed by Int kinetics.