ELECTROCHEMICAL POLYMERIZATION OF ANILINE IN PHOSPHORIC ACID AND THE PROPERTIES OF POLYANILINE

The behavior of the electrochemical polymerization of aniline in a weak acid, phosphoric acid, is very similar to that in strong acids, i.e. its polymerization rate increases quickly with the electrolysis time. The FTIR spectra of polyaniline samples synthesized in phosphoric acid indicate that the counter ion H2PO4^- is present in both the oxidized form and the reduced form of polyaniline. The counter ion plays an important role in adjusting the pH value at the electrode surface of polyaniline during the oxidation and reduction processes. As a result, a pair of redox peaks still appear in cyclic voltammograms of polyaniline in a solution of sodium sulfate of pH 5.5 and in a solution of NaH2PO4 of pH 7.0,respectively, at low potential scan rate; and the color of polyaniline film also changes with applied potential at pH 7.0. Thus,the pH region for the electrochemical activity and the electrochromism of polyaniline is extended to pH 5.5 for a solution of sodium sulfate and to pH 7.0 for a solution of NaH2PO4. The conductivity of polyaniline is 3.3 S cm^-1, depending on the concentration of phosphoric acid used in the stage of polymerization of aniline. The result of elemental analysis of polyaniline is presented here.

ELECTROCHEMICAL POLYMERIZATION OF ANILINE IN PHOSPHORIC ACID AND THE PROPERTIES OF POLYANILINE*

The behavior of the electrochemical polymerization of aniline in a weak acid, phosphoric acid, is very similar to that in strong acids, i.e. its polymerization rate increases quickly with the electrolysis time. The FTIR spectra of polyaniline samples synthesized in phosphoric acid indicate that the counter ion H2PO4- is present in both the oxidized form and the reduced form of polyaniline. The counter ion plays an important role in adjusting the pH value at the electrode surface of polyaniline during the oxidation and reduction processes. As a result, a pair of redox peaks still appear in cyclic voltammograms of polyaniline in a solution of sodium sulfate of pH 5.5 and in a solution of NaH2PO4 of pH 7.0,respectively, at low potential scan rate; and the color of polyaniline film also changes with applied potential at pH 7.0. Thus,the pH region for the electrochemical activity and the electrochromism of polyaniline is extended to pH 5.5 for a solution of sodium sulfate and to pH 7.0 for a solution of NaH2PO4. The conductivity of polyaniline is 3.3 Scm-1, depending on the concentration of phosphoric acid used in the stage of polymerization of aniline. The result of elemental analysis of polyaniline is presented here.