Effect of Si3N4 on chemical durability of chalcogenide glass

Chemical durability of the Si₃N₄ doped (up to 0.5 wt%) chalconitride glasses was evaluated by weight losses of glass samples after immersion in deionized water, H₂SO₄, HCl and NaOH solutions. IR spectra and SEM were used as an aid to examine the surface structure of corroded glass samples. Weight loss measurements showed a poorer stability of non-oxide glasses in basic solution than in acid solution, and the Si₃N₄ doping was found to improve chemical durability. Comparison of IR spectra of samples exposed to the basic solution with their original ones suggested the higher content of OH⁻ in its reaction layers, indicating that the corrosion of the present non-oxide glasses in the basic solution may result from the breakdown of the bridging Se due to an attack launched by OH⁻. The SEM evidence confirmed that Si₃N₄ doping did hinder the OH⁻ attacks on Ge and/or As, which is most likely related to incorporation of the three-coordinated N into the glass network, as supported by a comparison of the IR transmitting spectrum between uncorroded chalconitride glass and undoped chalcogenide glass.