p型透明导电氧化物CuCr1-x Cax O2的制备与光电性质研究 |
| |
作者单位: | 中国科学技术大学内耗与固体缺陷重点实验室,合肥,230026;中国科学技术大学内耗与固体缺陷重点实验室,合肥,230026;中国科学技术大学内耗与固体缺陷重点实验室,合肥,230026 |
| |
摘 要: |
|
关 键 词: | Ca掺杂CuCrO2 铜铁矿 p型导电氧化物 |
The Prepration of p-Type Transparant Conducting Oxides CuCr1-x CaxO2 and Research about Its Electrical and Optical Property |
| |
Authors: | Huang Hua Zhu Changfei Liu Wei |
| |
Institution: | {{each article.affiliations aff i}}
{{if aff.addressEn && aff.addressEn != ""}}
{{if aff.label && aff.label != "" && article.affiliations.length != 1}}{{@ aff.label}}.{{/if}}{{@ aff.addressEn}}{{/if}}
{{/each}} |
| |
Abstract: | Transparant conducting oxides showing the combination of high electrical conductivity and high transparency for visible light have been based on electron doping into a conduction band. For p-type delafossite oxides,the valence band is commonly the oxygen 2p band. Doping to produce holes in this band but the electronic conductivity of such p-type oxides is highly activated and can generally only be measured at temperatures well above room temperature. So it is very desirable to improve conductivity by doping wide-gap delafossites as transparant conducting oxides nowadays. The article reported the prepration and characterization of Ca-doped CuCrO2 monophasic delafossites. It was found that conductivity had a notable improvement after Ca-doped and reached 3. 2×10-2 S/cm for x=0.06 Ca-doped at room temperature and the structures had not been changed. The temperature dependence of electrical conductivity around room temperture was consistent with thermal activation type very well from 200 K to 300 K. The activation energe was 0. 36 eV before doping,but it changed to 0.27 eV when Ca-doped. This phenomenon suggest that in pure non-doped CuCrO2,carrier was the Cu+ d. After Ca-doped,the Cu2+ was formed from the Cu+ by a charge compensating process when the divalent Ca2+ substituted for the trivalent Cr3+ . The Seebeck coefficients being large positive constants implied that all the samples were p-type conducting oxides. |
| |
Keywords: | Ca-doped CuCrO2,Delafossite,p-type conducting oxides |