Thermal behaviour of high surface area V2O5/TiO2 catalysts

Thermal analysis (TG and DTA) was employed for the characterization of V₂O₅/TiO₂ catalysts supported on high surface area TiO₂. The results obtained are consistent with a uniform spreading of vanadium oxide on TiO₂ surface for V₂O₅ content less than 15% by weight.The presence of V₂O₅ on the surface of TiO₂ affects the anatase-rutile phase transition lowering the temperature at which it occurs.DTA measurements, performed on catalysts after many months from the preparation, show the appearance of an exothermic peak in the range 280°–340°C. This signal has been related to the oxidation of V(IV) to V(V) on the catalyst surface.Catalysts characterization, performed by chemical analysis and FT-IR spectroscopy, has confirmed this interpretation.It has been suggested that a slow modification of the catalyst occurs, leading to an increase of the V(IV) content during the time.

---

Zusammenfassung Zur Charakterisierung von V₂O₅/TiO₂-Katalysatoren auf hochoberflächigem TiO₂ Trägermaterial wurde die Thermoanalyse (TG und DTA) angewendet. Für einen V₂O₅-Gehalt von weniger als 15 Gew.% entsprechen die erhaltenen Ergebnisse einer gleichmäßigen Verteilung des Vanadiumoxides an der TiO₂-Oberfläche.Die Gegenwart von V₂O₅ an der Oberfläche von TiO₂ beeinflußt die Anatas-Rutil-Phasenumwandlung, indem sie die zugehörige Temperatur verringert.DTA-Messungen an Katalysatoren mehrere Monate nach ihrer Herstellung zeigten das Auftreten eines exothermen Peaks im Bereich 280°–340°C. Dieses Signal wurde der Oxidation von V(IV) zu V(V) an der Katalysatoroberfläche zugeschrieben.Diese Interpretation konnte durch eine Charakterisierung des Katalysatoren durch chemische Analyse und FT-IR-Spektroskopie bestätigt werden.Es wurde angedeutet, daß der Katalysator mit der Zeit einer langsamen Modifikation unterliegt, die zu einem Ansteigen des V(IV)-Gehaltes führt.