Synthesis of ultrafine yttrium aluminum garnet using sol-gel technology

Mesoporous yttrium aluminum garnet Y₃Al₅O₁₂ powders were prepared using sol-gel technology proceeding from solutions of metal alkoxoacetylacetonates. Xerogel microstructure was studied by SEM, and the fact of mesopores being formed was established. The temperature range within which Y₃Al₅O₁₂ crystallizes in a dynamic mode from the xerogel was determined to be 850?C950°C using an SDT Q600 TGA/DTA/DSC analyzer. A 1-h isothermal treatment of the xerogel was shown to reduce the garnet phase formation temperature to 800°C. At lower temperatures (400, 450 or 500°C), even long-term (6-h) calcination yielded X-ray amorphous powders with developed surfaces (specific surface areas were 230?C350 m²/g). Powder particle coarsening was studied upon sintering for 2 and 4 h at 1000, 1200, and 1400°C.