Effect of laser irradiation on the electrical properties of dysprosium doped LiCo-Ferrite

The effect of laser irradiation on the electrical properties of Li_0.5+z Co _z Dy _x Fe_2.5?2z?x O₄ ferrite (0.0 ≤ x ≤ 0.2, z = 0.1) has been studied in the temperature range 300 K ≤ T ≤ 750 K at frequencies of 10 kHz?5 MHz, using a LIMO-IR laser diode, at a wavelength of 808 nm. It was found that laser irradiation increases the polarization, the resistivity and the paramagnetic region. As the result of electronic rearrangement and lattice defects, small polorons and clusters were created. The doping of LiCo-Ferrite by Dy³⁺ increases both the AC and DC resistance of the investigated material. The variation of the AC and DC resistance with the Dy-content (x) obeys the following correlations R _ac/100 = 50x ²+4x+0.005 and R _dc/1000 = 31x ²+0.099x+0.09, respectively. A peculiar behaviour was obtained for the sample with Dy-content x = 0.075, as the resistance notably decreases. The applicable result is that laser irradiation increases the resistance of LiCo-ferrite by about 17% while its doping by dysprosium at x = 0.15 increases the resistance by about 23%. Its value is nearly stable for the temperature range from 340 to 480 K.