| Abstract: | The free volume of the microvoids in the polyimide samples, irradiated with 6 MeV electrons, was measured by the positron annihilation technique. The free volume initially decreased the virgin value from ～13.70 to ～10.98 Å3 and then increased to ～18.11 Å3 with increasing the electron fluence, over the range of 5?×?1014 – 5?×?1015 e/cm2. The evolution of gaseous species from the polyimide during electron irradiation was confirmed by the residual gas analysis technique. The polyimide samples irradiated with 6 MeV electrons in AgNO3 solution were studied with the Rutherford back scattering technique. The diffusion of silver in these polyimide samples was observed for fluences >2?×?1015 e/cm2, at which microvoids of size ≥3 Å are produced. Silver atoms did not diffuse in the polyimide samples, which were first irradiated with electrons and then immersed in AgNO3 solution. These results indicate that during electron irradiation, the microvoids with size ≥3 Å were retained in the surface region through which silver atoms of size ～2.88 Å could diffuse into the polyimide. The average depth of diffusion of silver atoms in the polyimide was ～2.5 μm. |