Czochralski-growth of germanium crystals containing high concentrations of oxygen impurities

Oxygen-containing germanium (Ge) single crystals with low density of grown-in dislocations were grown by the Czochralski (CZ) technique from a Ge melt, both with and without a covering by boron oxide (B₂O₃) liquid. Interstitially dissolved oxygen concentrations in the crystals were determined by the absorption peak at 855 cm⁻¹ in the infrared absorption spectra at room temperature. It was found that oxygen concentration in a Ge crystal grown from melt partially or fully covered with B₂O₃ liquid was about 10¹⁶ cm⁻³ and was almost the same as that in a Ge crystal grown without B₂O₃. Oxygen concentration in a Ge crystal was enhanced to be greater than 10¹⁷ cm⁻³ by growing a crystal from a melt fully covered with B₂O₃; with the addition of germanium oxide powder, the maximum oxygen concentration achieved was 5.5×10¹⁷ cm⁻³. The effective segregation coefficients of oxygen in the present Ge crystal growth were roughly estimated to be between 1.0 and 1.4.