| Abstract: | Dynamic viscoelastic properties of ladder polyorganosiloxanes have been studied by the method of induced resonance oscillations in the temperature range from –150 to 300°C and in the frequency range from 8 to 300 Hz. Two broad maxima of mechanical losses were observed for all the polymers studied independently of their chemical structure, a low-temperature maximum in the –150 to 0°C region and a high-temperature maximum in the 0 to 250°C region. It was found that the introduction of alkyl groups into polyphenylsilsesquioxanes does not noticeably affect the position and nature of the low-temperature relaxation peaks but in certain cases leads to an increase in the dynamic modulus in polyphenylalkylsilsesquioxanes, compared with the modulus of polyphenylsilsesquioxane in the same temperature region. In the high-temperature region, a distinct dependence is observed of the relaxation peak on the length and the content of alkyl groups in the polymer. It has been found that increase in the length and the content of alkyl groups is accompanied by a shift in the peak in the direction of low temperatures and a decrease in the value of the modulus. Hypotheses have been suggested on the nature of the shifts which lead to the relaxation peaks observed in the ladder polyorganosiloxanes.Institute of Heteroorganic Compounds, Academy of Sciences of the USSR, Moscow. Translated from Mekhanika Polimerov, No. 5, pp. 804–809, September–October, 1973. |