Moisture effects on the glass transition and the low temperature relaxations in semiaromatic polyamides

The influence of moisture absorption on the primary (glass) transition (T_a or T_g) and the low temperature relaxations of semiaromatic amorphous polyamides synthesized by isomeric aliphatic diamine and metha or para oriented phthalicdiacids has been investigated by means of differential scanning calorimeter (DSC) and dynamic mechanical thermal analyser (DMTA). The glass transition of semiaromatic polyamides was lowered due to the water absorption, and the β and the γ relaxations were as well. From the observed T_g and the difference in the heat capacity, the calculated T_g depression per 1 wt % water content was 12.3 K and the result was in good agreement with the experimental data. The depression of the glass transition may be expressed by the same manner as the plasticization of nylon 6 by water. The depressed β relaxation observed in the specimen containing a few percent of moisture was splitted into two transitions due to the reduction of water content, of which one was the elevation of the T_β and another was the simultaneous appearance of the T_γ, and then the single T_γ solely was observed for the completely dried specimen. The T_γ seemed to be merged into or not to be observed by the large and broad T_β transition when the sample was governed by a few percent of water, then it was emerged from the T_β due to water desorption. Thus, the T_β is believed to arise from the intermolecular hydrogen bonding between water molecules or between water and amide groups in wet polyamides. In addition, the γ relaxation originated from the peptide groups is attributable to the inter- and intramolecular hydrogen bonding between amide groups. © 1997 John Wiley & Sons, Inc. J Polyn Sci B: Polym Phys 35: 807–815, 1997