Facilitated Transport of C2H4 in a SiO2-poly(N-vinylpyrrolidone)-Ag+ Inorganic-Organic Hybrid Membrane

Inorganic-organic hybrid membranes containing silica as the structure matrix, poly(N-vinylpyrrolidone) (PVP) as the organic mediating agent and silver ions as olefinic carriers were prepared using sol–gel method and dip-coating process. The structure and permeances of the membranes for N₂, He, C₂H₄, C₂H₆ at different temperatures indicated that defect-free membranes were obtained and the transportation of the C₂H₄ through the membranes followed the dissolution and diffusion mechanism. Ideal separation factors of C₂H₄/C₂H₆ through the membranes were evaluated at the temperature of 298, 373 and 423 K respectively using mixture gas of 50% C₂H₄-50% C₂H₆. The results showed that the ideal separation factors of C₂H₄/C₂H₆ through the membranes were obviously greater than the ratio of PC₂H₄/PC₂H₆ obtained from the single gas measurement due to the hindering effect by the adsorbed C₂H₄. The ideal separation factors of C₂H₄/C₂H₆ increased with temperature and reached 10 at 423 K, which suggested that C₂H₄ and C₂H₆ could be separated at lower humidity compared to the reported organic polymer/silver salt membranes in which humidified gases and higher silver loading were usually used. The transport of C₂H₄ in the inorganic-organic hybrid membrane was proposed to follow the hopping mechanism, that is, olefins moved across the fixed silver sites.