Improvement of electrochemical performance of all-solid-state lithium secondary batteries by surface modification of LiMn2O4 positive electrode

To improve the electrochemical performance of an all-solid-state In/80Li₂S⋅20P₂S₅ (electrolyte)/LiMn₂O₄ cell, a lithium-titanate thin film was used to coat LiMn₂O₄. The interfacial resistance between LiMn₂O₄ and the electrolyte (measured after initial charging) decreased when the LiMn₂O₄ particles were coated with lithium-titanate. A cell with lithium-titanate-coated LiMn₂O₄ had a higher capacity than a cell with noncoated LiMn₂O₄ for current densities in the range 0.064 to 2.6 mA cm^− 2. Additionally, a cell with coated LiMn₂O₄ retained 96% of the 10th-cycle reversible capacity at a current density of 0.064 mA cm^− 2 after 50 cycles.