Effect of cation doping on ionic and electronic properties for lanthanum silicate-based solid electrolytes

Electronic as well as ionic conducting properties for oxyapatite-type solid electrolytes based on lanthanum silicate, La_9.333 + xSi₆O_26 + 1.5x (LSO) were investigated in the oxygen-excess region (x > ca. 0.3). We have found that the oxygen excess-type LSO (OE-LSO), namely La₁₀Si₆O₂₇ on weighted basis, exhibited high conductivity, and substitution of the Si-site of LSO with some dopants (Mⁿ⁺) had a positive effect toward the conducting property. Furthermore, it was also found that addition of a very small amount of iron ions into the M-doped OE-LSO, La₁₀(Si_6-yMⁿ⁺_y)O_27-(2-0.5n)y, improved its conductivity. On the other hand, replacement of the La-site with various ions for La₁₀(Si_6-yMⁿ⁺_y)O_27-(2-0.5n)y did little to improve conductivity. The electronic transport numbers for Al-doped OE-LSO with Fe-addition, (1-α){La₁₀(Si_5.8Al_0.2)O_26.9}-α(FeO_γ), evaluated with the Hebb-Wagner polarization method were very low: i.e., 1.1 × 10^− 3 and 2.9 × 10^− 3 under P(O₂) = 1.1 × 10⁴ Pa at 1073 K for α = 0.00 and 0.005, respectively. Conductivity for each sample was unchanged under humidified atmosphere at 1073 K sustained for over 50 h, revealing that both compositions were chemically stable. It was concluded that 0.995{La₁₀(Si_5.8Al_0.2)O_26.9}-0.005(FeO_γ) is suitable for the fuel cell electrolytes because of its high and almost pure ionic conductivity, and its good chemical stability under humidified as well as reducing conditions.