ZrO_2-Al_2O_3复合氧化物的合成及其性能研究

采用表面活性剂改性的沉淀法合成了系列掺杂钇、镧、钡的氧化锆铝复合氧化物。通过XRD、XRF、低温N2吸附和CO脉冲化学吸附等手段考察了表面活性剂、助剂、焙烧温度对复合材料结构、孔结构以及负载0.5%铑催化剂的分散性能等的影响。研究表明:与采用常规沉淀法合成的氧化锆铝复合氧化物相比,添加表面活性剂合成的样品具有更大的比表面积、孔容和适合的孔径分布。分别或同时掺杂La、Ba、Y合成的氧化锆铝复合氧化物都能抑制氧化铝的α相变,提高复合材料和催化剂表面金属Rh的高温抗烧结能力,特别是同时掺杂La、Ba、Y合成的Rh/LBYZA样品经1100℃4h焙烧后仍有17.82%的金属分散度。以LBYZA为载体制备的新鲜催化剂(600℃4h焙烧样品)在CO选择还原NO反应中NO和CO的起燃温度分别为240、243℃,完全燃烧温度分别为273、280℃,表现出较高的催化活性。

Preparation of ZrO2-Al2O3 Mixed Oxides and Study on Their Properties

A series of ZrO2-Al2O3 mixed oxides with La, Ba and Y were prepared by co-precipitation method which modified by surfactant. The samples were characterized by XRD, XRF, BET measurements and CO pulse chemiadsorption. The effect of surfactant, promoter and calcination temperature on structure, pore structure of these materials and dispersion of Rh on composite supports was investigated. It was found that compared with materials prepared by conventional co-precipitation method, the samples prepared by new meth...